C67500
C67500 Spec SheetC67500 possesses good torsional properties and general corrosion resistance. Manganese bronze withstands exposure to dry gases, dilute alkalis, sulphides, and most organic solvents and acids. Though C67500 has common resistance, contact with ammonia, mercury, and most chlorine gas should be avoided.
Chemical Composition
| Elements | Min (%) | Max (%) |
|---|---|---|
| Cu | 57.00 | 60.00 |
| Pb | – | 0.20 |
| Sn | 0.50 | 1.50 |
| Al | – | 0.25 |
| Fe | 0.80 | 2.00 |
| Mn | 0.05 | 0.50 |
| Total Others | – | 0.50 |
| Zn | Remainder | |
Mechanical properties according to ASTM B138 (as per temper HO2)
| Range (inch) | UTS Min (ksi) |
UTS Max (ksi) |
PS Min (ksi) |
Elongation Min (%) |
Hardness | ||
|---|---|---|---|---|---|---|---|
| Hardness Min (HRB) |
Hardness Max (HRB) |
||||||
| Round (Dia) | 0.059 – 1.000 | 72 | – | 36 | 13 | – | – |
| 1.000 – 20.000 | 70 | – | 35 | 15 | – | – | |
| 2.500 – 2.953 | 65 | – | 32 | 17 | – | – | |
| Hex (A/F) | 0.118 – 1.000 | 72 | – | 36 | 13 | – | – |
| 1.000 – 2.000 | 70 | – | 35 | 15 | – | – | |
| 2.500 – 2.756 | 65 | – | 32 | 17 | – | – | |
| Square (A/F) | 0.118 – 1.000 | 72 | – | 36 | 13 | – | – |
| 1.000 – 2.362 | 70 | – | 35 | 15 | – | – | |
| Rectangle Thickness | 0.118 – 1.000 | 72 | – | 36 | 13 | – | – |
| 1.000 – 1.968 | 70 | – | 35 | 15 | – | – | |
| Range (mm) | UTS Min (MPa) |
UTS Max (MPa) |
PS Min (MPa) |
Elongation Min (%) |
Hardness Min (HRB) |
Hardness Max (HRB) |
||
|---|---|---|---|---|---|---|---|---|
| Round (Dia) | 1.5 | 25 | 500 | – | 250 | 13 | – | – |
| 25 | 65 | 450 | – | 240 | 15 | – | – | |
| 65 | 75 | 450 | – | 220 | 17 | – | – | |
| Hex (A/F) | 3 | 25 | 500 | – | 250 | 17 | – | – |
| 25 | 65 | 45 | – | 240 | 15 | – | – | |
| 65 | 70 | 450 | – | 220 | 17 | – | – | |
| Square (A/F) | 3 | 25 | 500 | – | 250 | 13 | – | – |
| 25 | 60 | 450 | – | 240 | 15 | – | – | |
| Rectangle Thickness | 3 | 25 | 500 | – | 250 | 13 | – | – |
| 25 | 50 | 450 | – | 240 | 15 | – | – | |
| PHYSICAL PROPERTIES | |
|---|---|
| Melting Point – Liquidus °F | 1630 |
| Melting Point – Solidus °F | 1590 |
| Density lb/cu in. at 68°F | 0.302 |
| Specific Gravity | 8.36 |
| Electrical Conductivity % IACS at 68°F | 24 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68°F | 61 |
| Coefficient of Thermal Expansion 68–572 × 10⁻⁶ per °F | 11.8 |
| Specific Heat Capacity Btu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES | |
|---|---|
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Good |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Good |
| Seam Weld | Fair |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | 80 |
| Machinability Rating | 30 |
Typical Uses
Automotive
Fasteners
Industrial